Web为了提高AZ91D镁合金的抗腐蚀性能,在其表面电镀Al-Zn复合镀层。研究了镀层的物相组成、微观形貌、结合力及抗腐蚀性能。结果表明,镀铝为中间层能得到较好的组织和性能,镀层表面为纯锌,镀Zn层分布致密均匀,镀锌层约6μm,中间铝层约4μm且组织疏松;电流密度3.5 A/dm^(2)、电镀时间1 min时镀层具有较好的 ... WebMar 28, 2024 · Figures 10 and 11 show the surface appearance of the AZ91D magnesium alloy substrate and the sample HT/170-7h after different immersion times, respectively. The AZ91D magnesium alloy substrate started to react as soon as it was immersed in 5 wt. % NaCl solution, and bubbles were generated on the surface.
Coating pretreatment for mg alloy az91d
Did you know?
WebJun 11, 2024 · It is therefore clear and evident that successful coating technology on Mg alloys needs appropriate pretreatments [13–15] . In practice, one of the most difficult … WebMar 12, 2012 · The vanadium based conversion coating (from a bath containing sodium metavanadate) as an effective pretreatment for electroless plating on AZ91D magnesium alloy has proposed by Sudagar et al. [24 ...
WebJul 3, 2007 · Zn–13 wt.% Ni coating provides very good corrosion protective function to inner AZ91D magnesium alloy. Phosphate–permanganate treatment enhances the corrosion resistance of Zn–Ni coatings. Introduction Magnesium is the lightest of all metals used as the base for constructional alloys. WebA double-layer coating was formed on AZ91D magnesium alloy by alkaline and subsequent acidic plating. The inner alkaline layer was composed of Ni–P coating with low P content, but the outer acidic layer consisted of Ni–P coating with high P content. The morphologies, composition and phase structure of the double-layer coating were ...
WebJul 1, 2012 · The influence of aluminum tri-polyphosphate on the protective behavior of Mg-rich epoxy coating on AZ91D magnesium alloy Xiangyu Lu, Y. Zuo, Xuhui Zhao, … WebA silane film is prepared on AZ91D magnesium alloy and the effect of the silane pretreatment on the performance of a Mg-rich primer on AZ91D alloy are studied. After the silane treatment, Si–O–Mg covalent bonds form between the silane film and magnesium substrate and Si–O–Si structure forms in the silane film.
WebCoating defects and coating failure upon Mg alloy AZ91D are usually due to non-uniform coating growth, which is intrinsically caused by the microstructural heterogeneity of the …
WebDec 23, 2024 · Alloy AZ91D is the most widely used magnesium die cast alloy and has an excellent ... pink sweater with red heartsWebJun 6, 2024 · R.X. Sun, S.K. Yang, and T. Lv, Corrosion behavior of AZ91D magnesium alloy with a calcium—phosphate—vanadium composite conversion coating, Coatings, 9 (2024), No. 6, art. No. 379. M.F. Morks, Magnesium phosphate treatment for steel, Mater. Lett., 58 (2004), No. 26, p. 3316. Article CAS Google Scholar pink sweater with pearlsWebMar 1, 2011 · Elsentriecy, et al.,42 proposed a new HF pickling pretreatment for AZ91D Mg alloy and explored the effect of this pickling pretreatment on the corrosion protection ability of the stannate conversion coating. The optimal condition reported to remove the surface oxide layer without severe damage to the surface was 0.25 wt% HCl + 0.25 wt% HF for … pink sweat honesty lyrics